SATURATED POLYESTER RESIN FOR POWDER COATING

WATER BASED ACRYLIC COPOLYMER EMULSION RESINS SOLVENT BASED ACRYLIC RESIN SOLID ACRYLIC RESINS WAX EMULSION AQUEOUS POLYURETHANE DISPERSION SATURATED POLYESTER RESIN FOR POWDER COATING ACRYLIC RESIN FOR POWDER COATING POLIVINYL ACETATE EMULSION ETHYLENE VINYL ACETATE COPOLYMER EMULSION LIQUID PHENOLIC RESIN HOT MELT ADHESIVES RESINS FOR COATING WOOD COATING & RESINS FOR COATING CONSTRUCTION

SATURATED POLYESTER RESIN FOR POWDER COATING>

SATURATED POLYESTER RESIN FOR POWDER COATING 


Main Ingredients│Hybrid Carboxyl-Terminated Polyester Resin
Main Application│Suitable for the powder coating industry
Speeial Features│Excellent leveling properties

 

Formulated for decorative and protective thermosetting powder coatings

 

          

 

CARBOXYLATED POLYESTER RESIN FOR HYBRID SYSTEMS

Product Code Acid Value Max. CI Viscosity Tg
(approx.) 		Cure Cond
(Substrate Temperature) 		Ratio
PE/EP 		Properties
EL-2800 23~29 3 200~350 54 10min/200°C 80/20 Provides typical performance with minimal epoxy content
EL-3310 70~85 3 100~250 60 10min/180°C 50/50 Good mechanical properties and film flexibility, widely used in 50/50 hybrid systems
EL-3320 70~85 3 100~250 60 10min/160°C 50/50 Excellent leveling, suitable for thin coating applications
EL-3650N 48~55 3 100~250 61 10min/200°C 60/40 Good leveling, suitable for thin-film powder coatings
EL-365N 48~55 3 100~200 61 10min/200°C 60/40 Especially suitable for tribo (frictional charging) systems
EL-5310 70~85 3 50~150 55 10min/180°C 50/50 Excellent leveling
EL-5500 48~55 3 50~200 57 10min/200°C 60/40 General-purpose 40/60 hybrid system
EL-5510 48~55 3 50~200 57 10min/180°C 60/40 General-purpose 40/60 hybrid system
TB-550 48~55 3 50~200 57 10min/200°C 60/40 Especially suitable for tribo (frictional charging) systems
EL-5500K 48~55 3 50~200 57 10min/200°C 60/40 Excellent leveling
EL-5700 28~36 3 100~250 59 10min/200°C 70/30 Excellent leveling
EL-5710 28~36 3 100~250 59 10min/180°C 70/30 Excellent storage stability, especially suitable for special texture coatings
EL-5720 28~36 3 100~250 59 10min/160°C 70/30 Excellent storage stability, especially suitable for special texture coatings
EL-570 28~36 3 100~250 59 10min/200°C 70/30 Especially suitable for tribo (frictional charging) systems
EL-571 28~36 3 100~250 59 10min/180°C 70/30 Especially suitable for tribo (frictional charging) systems
EL-5810N 30~38 3 300~400 64 10min/180°C 70/30 Good leveling, general-purpose 70/30 hybrid system

 

CARBOXYLATED POLYESTER RESIN FOR TGIC SYSTEMS TGIC

Product Code Acid Value Max. CI Viscosity Tg
(approx.) 		Cure Cond
(Substrate Temperature) 		Ratio
PE/EP 		Properties
EL-6100 48~55 2 50~200 60 10min/200°C 90/10 Can be blended with EL-6300 (50/50) to produce semi-matte powder coatings
EL-6300 11~26 2 200~400 63 10min/200°C 96/4 Suitable for semi-matte and TGIC system applications
EL-6400 28~36 2 250~450 64 10min/200°C 93/7 Superior weather resistance
EL-6500 28~36 2 150~350 62 10min/200°C 93/7 Excellent balance of leveling and mechanical properties, great storage stability, general-purpose TGIC system
EL-6510 28~36 2 150~350 62 10min/180°C 93/7 具Excellent balance of leveling and mechanical properties, great storage stability, general-purpose TGIC system
EL-6600 28~36 2 150~350 60 10min/200°C 93/7 Excellent leveling, suitable for thin coating applications
EL-660 28~36 2 150~350 60 10min/200°C 93/7 Especially suitable for tribo (frictional charging) systems
EL-660B 28~36 2 150~350 60 10min/200°C 93/7 Especially suitable for tribo systems, ideal for aluminum curtain wall applications
EL-6700 28~36 2 400~600 65 10min/200°C 93/7 Good weather resistance, general-purpose TGIC system
EL-6700A 28~36 2 505~600 65 10min/200°C 93/7 Improved bake resistance compared to EL-6700

 

CARBOXYLATED POLYESTER RESIN FOR TGIC SYSTEMS

Product Code Acid Value Max. CI Viscosity Tg
(approx.) 		Cure Cond
(Substrate Temperature) 		Ratio
PE/EP 		Properties
TB-670 28~36 2 400~600 65 10min/200°C 93/7 Especially suitable for tribo (frictional charging) systems
TB-670N 28~36 2 400~600 65 10min/200°C 93/7 Especially suitable for tribo systems, with improved leveling compared to TB-670
EL-6800 28~36 2 150~350 62 10min/200°C 93/7 Good leveling, film appearance, and high pigment loading capability
EL-6810 28~36 2 150~350 60 10min/180°C 93/7 Good leveling, film appearance, and high pigment loading capability
EL-6820 28~36 2 150~350 60 10min/160°C 93/7 Good leveling, film appearance, and high pigment loading capability
TB-680 28~36 2 150~350 60 10min/200°C 93/7 Especially suitable for tribo (frictional charging) systems
TB-710 28~36 2 200~350 60 10min/180°C 93/7 Superior leveling and Triboelectric charging system
EL-7700 28~36 2 50~150 62 10min/200°C 93/7 Good balance of leveling and mechanical properties, with excellent storage stability
EL-7720 28~36 2 100~200 62 10min/160°C 93/7 Good balance of leveling and mechanical properties, with excellent storage stability
Please contact us for details.